Microstructure and Phase Evolution of Cement-Bonded High-Alumina Refractory Castables for Porous Purging Plugs

Q. Wang, Y. Li, N. Xu, R. Xiang, S. Li

Journal of Ceramic Science and Technology, Vol. 9, No. 1 (2018), pp. 1-6

DOI: 10.4416/JCST2017-00044

Download full article (PDF)

Abstract

This work addresses the microstructure and phase evolution of four designed high-alumina refractory castables (containing ρ-Al2O3 or calcium aluminate cement as a binder source and 0 or 1 wt% microsilica). Various experimental tests (air permeability, linear change rate, apparent porosity, cold modulus of rupture, cold crushing strength, hot modulus of rupture, pore size distribution, X-ray diffraction and scanning electron microscopy) were conducted to characterize the castables. The results show that using cement as the binder has a significant effect on the properties of the refractory castables. The cement-bonded castables exhibited a lower linear shrinkage rate, apparent porosity and air permeability, higher cold modulus of rupture and cold crushing strength, as well as a smaller mean pore size than that of the ρ-Al2O3-bonded castables. The results were attributed to the formation of calcium hexaluminate. Some CA6 was detected inside the pores, which occupied space in the pores and prevented the formation of interconnected pores, while some CA6 existed outside the pores, which enhanced the densification of the structure and reduced the size of pores. Moreover, the addition of microsilica can facilitate interconnected pore formation in cement-bonded castables, but lower the hot modulus of rupture owing to the formation of low-melting-temperature phase (C2AS).

Keywords

Cement, porous purging plug, microstructure, phase evolution, pore size distribution